Lab Volume

HKY-60 ：108L

HKY-90 ：270L

HKY-120 :640

Equipment Material

The out side shell is made of light gray PVC board with a thickness of 5mm and a durable temperature of 70 °C. The edge is surrounded by a three-dimensional reinforcing thickness of 8mm, and the structure is firm; the test chamber cover is sealed with a transparent acrylic impact-resistant plate with a thickness of 5mm. The inner and outer edges of the edge are thickened to prevent distortion due to long-term high temperature. The thickness is 12mm.

Temperature Range

35o C-55o C

Temperature Fluctuations

≤ ± 0.5o C

Temperature Uniformity

≤ ± 2o C

Temperature Precision

± 1o C

Brine Temperature

35o C± 1o C

PH

Salt Spray Method (NSS ACSS6.5~7.2)   Corrosion-resistant Testing Method(CASS)3.0~3.2

Spray Quantity

1.0~2.0 ml / 80cm2 / hr

Test Chamber Temperature

Salt spray test; NSS, ACSS:Laboratory: 35 ° C ± 1 ° C.
Corrosion resistance test: CASS:Laboratory: 50 °C ± 1 °C.

Saturated air Barrel Temperature

Salt spray test; NSS, ACSS:Pressure air tank: 47 ° C ± 1 ° C
Corrosion resistance test: CASS:Pressure air tank: 63 ° C ± 1 ° C

Spray Quantity

1~2ml/h adjustable (ml/80cm2/h standard requires testing for 16 hours to get average amount)

Power

220V  Single Phase 3.0KW 50HZ

Multiple Safety Protection Devices

Current discharge protection, over pressure protection, over temperature protection, over load fuse protection

Accessories

Testing Salt/ Measuring tank/ Equipment   each 1 set

Standard

CNS: 3627, 3385, 4159, 7669, 8886; JIS: D0201, H8502, H8610, K5400, Z2371; ISO: 3768, 3769, 3770; ASTM: B117, B268